Why is tungsten difficult to machine?

Tungsten is extremely hard, dense, and abrasive. It requires specialized carbide or diamond tooling, negative rake angles, low cutting speeds, and rigid setups. Heat generation is significant and must be managed to prevent tool failure.

What tungsten grades are most commonly machined?

Heavy-metal tungsten alloys (90-97% W) are the most commonly machined grades. They are easier to machine than pure tungsten while retaining high density and strength. Pure tungsten is more difficult and is used for specialized applications like electrodes and filaments.

What is the difference between pure tungsten and heavy metal tungsten?

Pure tungsten is 99.95% W with high melting point but poor machinability. Heavy metal tungsten is alloyed with nickel, iron, or copper for improved machinability while maintaining high density (90-97% W). Heavy metal tungsten is used for counterweights, shielding, and precision parts.

What are the common applications of CNC tungsten machining?

Radiation shielding (medical CT, X-ray, nuclear medicine), aerospace counterweights, gyroscope components, electrical welding and EDM electrodes, and industrial tooling.

What cutting tool material is recommended for tungsten?

CBN, PCD, or carbide tooling with CBN or PCD inserts. Sharp, positive rake geometry for turning and small corner radii for milling.

What safety considerations are required for tungsten machining?

Tungsten is a heavy metal and requires proper dust control and PPE to prevent exposure. Proper coolant management is required for heat dissipation and chip control.

CNC Tungsteno | Servicios de mecanizado de precisión de tungsteno

Nuestros Servicios de Mecanizado CNC

From prototype to production — reliable quality, on-time delivery

Ofrecemos servicios de mecanizado CNC de precisión para una amplia gama de materiales incluyendo aluminio, acero, acero inoxidable, cobre, latón, titanio, PEEK, PTFE, acetal, nylon y otros plásticos de ingeniería. Nuestras capacidades de fabricación cubren fresado CNC de 3 ejes, 4 ejes y 5 ejes, así como torneado CNC, adecuado tanto para el desarrollo de prototipos como para series de producción de alto volumen.

Con la certificación ISO 9001:2015 y un compromiso con la calidad, atendemos a clientes en las industrias aeroespacial, automotriz, médica, electrónica, equipos industriales y bienes de consumo. Nuestras capacidades internas incluyen acabado superficial, anodización, recubrimiento en polvo, tratamiento térmico e inspección con CMM y equipos de medición óptica.

Ofrecemos precios competitivos, plazos de entrega flexibles y trazabilidad completa del material. Desde soportes simples hasta componentes de precisión complejos, entregamos piezas que cumplan con sus especificaciones con calidad fiable y entrega puntual.

Estudios de casosMás+

5-axis machining of special-shaped parts

Mecanizado de 5 ejes de piezas de forma especial-aluminio

SLM 3D Printed Aluminum Alloy Turbo Compressor Impeller with Precision Bored Mounting Bore

SLM 3D impreso aleación de aluminio turbocompresor impulsor con precisión perforado montaje perforación-aluminio

Precision 6061 Aluminum Milled Star-Shaped Adapter Flange with Electroless Nickel Plating

Precisión 6061 aluminio fresado en forma de estrella adaptador brida con electroless níquel chapado-aluminio

Precision POM Medical Test Cover Plate with Dimensional Stability and Defect-Free Surface Control

Placa de cubierta de prueba médica de precisión POM con estabilidad dimensional y control de superficie libre de defectos

Custom Aluminum 6061 Part CNC Milling Machining Service

Servicio de mecanizado de fresado CNC de aluminio personalizado 6061

Precision 6061-T6 Semiconductor Optical Inspection Module Base Housing with Coaxiality Control

Precisión 6061-T6 Semiconductor Cámara de base del módulo de inspección óptica con control de coaxialidad-aluminio

Materiales

Aluminio 5083-H111

CNC Aluminum 5083-H111 | 3.3547 | 54300| AlMg4.5Mn0.7

Aluminio 5083 - h111 | 3.3547 | 54.300 | almg4.5mn0.7

El aluminio 5083 (cnc) es una aleación de aluminio endurecida por tensión con excelente resistencia a la corrosión. Adecuado para aplicaciones marinas. Se puede soldar.

Comprender Aluminio 5083-H111

Aluminio 6063

CNC Aluminum 6063 | EN AW-6063 | 62400| AlMg0,7Si

Aluminio 6063 | EN AW-6063 | 62400 | AlMg0,7Si

El aluminio 6063 tiene buenas propiedades mecánicas y puede ser tratado térmicamente. Adecuado para aplicaciones aeroespaciales. Se puede soldar.

Comprender Aluminio 6063

Aluminio 5052

CNC Aluminum 5052 | EN AW-5052 | 3.3523 | AlMg2,5

Aluminio 5052 | EN AW-5052 | 3.3523 | AlMg2,5

El aluminio 5052 es una aleación de aluminio endurecida por deformación con excelente resistencia a la corrosión. Adecuado para aplicaciones marinas. Se puede soldar.

Comprender Aluminio 5052

Aluminio 2024-T351

CNC Aluminum 2024-T351 | 3.1355 | 24530 | AlCu4Mg1

Aluminio 2024-T351 | 3.1355 | 24530 | AlCu4Mg1

El aluminio 2024 es una aleación de alta resistencia con excelente resistencia a la fatiga. Adecuado para aplicaciones aeroespaciales.

Comprender el aluminio 2024-T351

Aluminio 7050

CNC Aluminum 7050 | EN AW-7050 | 3.4144| AlZn6CuMgZr

Aluminio 7050 | EN AW-7050 | 3.4144 | AlZn6CuMgZr

El aluminio 7050 tiene excelentes propiedades mecánicas con buena ductilidad, alta resistencia, tenacidad y buena resistencia a la fatiga. Adecuado para aplicaciones aeroespaciales.

Comprender Aluminio 7050

Aluminio MIC-6

Aluminio mic6

El aluminio mic6 es un material ligero que se puede mecanizar fácilmente a alta velocidad y sin tensión, contaminantes y poros.

Comprender MIC-6 de aluminio

Aluminio 6082-T651

CNC Aluminum 6082-T651 | 3.2315 | 64430 | AlSi1MgMn

Aluminio 6082-T651 | 3.2315 | 64430 | AlSi1MgMn

La composición y las propiedades del aluminio 6082 - t651 (cnc) son muy similares a las de 6061, con una resistencia a la tracción ligeramente superior. Cumple con los estándares británicos.

Comprender el aluminio 6082-T651

Aluminio 2017A

CNC Aluminum 2017A | 3.1325 | 24530 | AlCu4MgSi

Aluminio 2017A | 3.1325 | 24530 | AlCu4MgSi

El Aluminio 2017 tiene una ductilidad y formabilidad más altas que el Aluminio 2014 y tiene una resistencia intermedia.

Comprender Aluminio 2017A

Aluminio 7075-T651

CNC Aluminum 7075-T651 | 3.4365 | 76528 | AlZn5.5MgCu

Aluminio 7075-T651 | 3.4365 | 76528 | AlZn5.5MgCu

El aluminio 7075-T651 (CNC) es un material de grado aeroespacial con una excelente relación resistencia-peso y resistencia y dureza comparables a los aceros. T651 es el temperamento del aluminio 7075, y para lograr este temperamento, la aleación se trata térmicamente con solución, alivia el estrés y luego envejece artificialmente.

Comprender Aluminio 7075-T651

Aluminio 2014

CNC Aluminum 2014 | 3.1255 | 24345 | AlCu4SiMg

Aluminio 2014 | 3.1255 | 24345 | AlCu4SiMg

El aluminio 2014 se mecaniza fácilmente y se puede endurecer para obtener fuerzas comparables al acero, pero es propenso a la corrosión. Adecuado para aplicaciones aeroespaciales.

Comprender Aluminio 2014

Aluminio 6061-T651

CNC Aluminum 6061-T651 | 3.3211 | 65028 | AlMg1SiCu

Aluminio 6061-T651 | 3.3211 | 65028 | AlMg1SiCu

El aluminio 6061-T651 se utiliza comúnmente en las industrias aeroespacial, automotriz y de la construcción debido a su alta resistencia, excelente maquinabilidad y buena soldabilidad. La designación "T651" indica que el material ha sido sometido a un tratamiento térmico para alcanzar un nivel específico de dureza.

Comprender el aluminio 6061-T651

Aluminio 7075-T7351

CNC Aluminum 7075-T7351 | 3.4365 | 76528 | AlZn5.5MgCu

Aluminio 7075 - t7351 3.4365 76.528 alzn5.5mgcu

El aluminio 7075-T7351 se emplea frecuentemente en aplicaciones aeroespaciales y de defensa, así como en los sectores automotriz y de transporte, debido a su elevada resistencia, excelente maquinabilidad y buena resistencia a la fatiga. La designación "T7351" indica que el material ha sido sometido a un tratamiento térmico para alcanzar un nivel específico de dureza.

Comprender Aluminio 7075-T7351

Aluminio 6061 - T6

CNC Aluminum 6061-T6 | 3.3211| 65028| AlMg1SiCu

Aluminio 6061 - T6 | 33211 | 65028 | almg1sicu

El aluminio 6061 (CNC) es la aleación de aluminio más popular. Tiene una buena relación resistencia-peso, excelente mecanizabilidad y resistencia natural a la corrosión.

Comprender Aluminio 6061-T6

Aluminio 6082

CNC Aluminum 6082 | 3.2315 | 64430| AlSi1MgMn

Aluminio 6082 | 3.2315 | 64430 | alsi1mgm

El aluminio 6082 (CNC) tiene composición y propiedades muy similares a 6061, con una resistencia a la tracción ligeramente mayor. Conforme a las normas británicas.

Comprender Aluminio 6082

Aluminio 6060

Aluminio 6060 | 33206 | almgsi

La aleación 6060 ofrece una buena resistencia, una resistencia a la corrosión relativamente buena y es adecuada para la anodización decorativa.

Comprender Aluminio 6060

Aluminio 7075 - T6

CNC Aluminum 7075-T6 | 3.4365 | 76528 | AlZn5,5MgCu

Aluminio 7075-T6 | 3.4365 | 76528 | AlZn5,5MgCu

El aluminio 7075-T6 (CNC) es un material de grado aeroespacial con una excelente relación resistencia-peso y resistencia y dureza comparables a los aceros.

Comprender Aluminio 7075-T6

Aplicación

Protección contra la radiación

Escudos de rayos X y CT
Contenedores de medicina nuclear
Colimatores de rayos gamma y blindaje
Componentes de radioterapia
Protección del reactor nuclear

Aeroespacial y Defensa

Contrapesos y pesos de equilibrio
Componentes del giroscopio
Piezas amortiguadoras de vibraciones
Inercia y componentes de masa
Penetradores de proyectiles

Dispositivos médicos

Componentes del tubo de rayos X
Cuchillas del colimator
Protección de radioterapia
Componentes del escáner CT

eléctrico

Electrodos de soldadura (gas inerte de tungsteno)
Electrodos EDM (cobre-tungsteno)
Contactos y interruptores eléctricos
Componentes de alta tensión

Industriales

Herramientas de apósito de ruedas de molienda
Componentes resistentes al desgaste
Instalaciones y herramientas de alta temperatura
Matrices de extrusión y dibujo

Capacidades

Mecanizamos aleaciones de tungsteno, principalmente grados de tungsteno de metal pesado (90-97% W) utilizados en aplicaciones aeroespaciales, médicas e industriales. El equipo incluye centros rígidos de fresado y torneado CNC con herramientas de carburo o CBN. Se requieren bajas velocidades de corte, alimentaciones positivas y configuraciones rígidas. Tolerancias mantenidas al estándar ±0.02-0.05mm. Certificado ISO 9001:2015 y AS9100D.

Acabados

Como mecanizado

Acabado estándar para piezas de tungsteno
Ra 1.6 – 3.2μm típico
Superficies funcionales

molienda

Acabado de precisión para tolerancias ajustadas
Utilizado para rodamientos y superficies de sellado
Ra 0,2 - 0,8 μm

Pulido

Acabado reflectante de alto brillo
Utilizado para contactos eléctricos y de precisión
Ra 0.4μm alcanzable

chorro de cuentas

Textura mate uniforme
Utilizado para la preparación de superficies
Apariencia industrial

Tratamiento térmico

Alivio de tensión después del mecanizado
Mejora la estabilidad dimensional
Requerido para piezas de tolerancia cercana

Especificaciones técnicas

Grado de tungsteno	W Contenido	Densidad (g/cm³)	Dureza (HRC)	Propiedades clave	Usos comunes
Tungsteno puro	99.95%	19.25	35-45	Alta temperatura, conductividad	Electrodos, filamentos, EDM
W-Ni-Fe (95%)	95%	18.0	25-30	Alta densidad, mecanizable	Contrapesos, blindaje
W-Ni-Cu (95%)	95%	18.0	25-30	No magnético	Medicina, aeroespacial
Cobre-Tungsteno	75-90%	15-17	20-25	Alta conductividad, resistencia al calor	Electrodos EDM, contactos

Parámetro	Tungsteno puro	Tungsteno de metal pesado
Resistencia a la tracción (MPa)	800-1,000	700-1,100
Resistencia al rendimiento (MPa)	500-700	400-900
Elongación en la ruptura (%)	5-15	2-10
Conductividad térmica (W/m·K)	170	160-180
Módulo de elasticidad (GPa)	400	300-350
Punto de fusión (°C)	3,422	2,800-3,000
Resistencia a la corrosión	Sobresaliente	Sobresaliente

Parámetro	Capacidad
Tamaño máximo de la pieza (fresado)	2.000 mm x 800 mm x 600 mm
Tamaño máximo de la pieza (girando)	600mm de diámetro x 1.500mm de longitud
Tolerancia estándar	±0.02 – 0.05mm
Tolerancia de precisión	± 0,01 mm
Acabado de superficie (como mecanizado)	Ra 1,6 - 3,2 μm
Acabado de superficie (tierra)	Ra 0,2 - 0,8 μm

Preguntas frecuentes

¿Por qué es difícil mecanizar el tungsteno?

El tungsteno es extremadamente duro, denso y abrasivo. Requiere herramientas especializadas de carburo o diamante, ángulos negativos de rastrillo, bajas velocidades de corte y configuraciones rígidas. La generación de calor es significativa y debe gestionarse para prevenir el fallo de la herramienta.
¿Qué grados de tungsteno se mecanizan más comúnmente?

Las aleaciones de tungsteno de metales pesados (90-97% W) son los grados más comúnmente mecanizados. Son más fáciles de mecanizar que el tungsteno puro al tiempo que conservan una alta densidad y resistencia. El tungsteno puro es más difícil y se utiliza para aplicaciones especializadas como electrodos y filamentos.
¿Cuál es la diferencia entre tungsteno puro y tungsteno de metal pesado?

El tungsteno puro es 99,95% W con alto punto de fusión pero mala maquinabilidad. El tungsteno de metal pesado se alea con níquel, hierro o cobre para mejorar la maquinabilidad mientras mantiene una alta densidad (90-97% W). El tungsteno de metal pesado se utiliza para contrapesos, blindajes y piezas de precisión.
¿Cuáles son las aplicaciones comunes del mecanizado de tungsteno CNC?

Protección contra radiaciones (CT médica, radiografía, medicina nuclear), contrapesos aeroespaciales, componentes de giroscopio, electrodos de soldadura eléctrica y EDM y herramientas industriales.
¿Qué material de herramienta de corte se recomienda para el tungsteno?

Herramientas de CBN, PCD o carburo con insertos de CBN o PCD. Geometría de rastrillo afilada y positiva para girar y pequeños radios de esquina para fresar.
¿Qué consideraciones de seguridad se requieren para el mecanizado de tungsteno?

El tungsteno es un metal pesado y requiere un control adecuado del polvo y EPI para prevenir la exposición. Se requiere una gestión adecuada del refrigerante para la disipación del calor y el control del chip.